پلی استال- مقاوم به ضربه
KOPLA Poly Acetal(POM) |
SORT |
Impact Modified Grade |
||
Name |
US12060 |
|||
Properties |
Test Method (ASTM) |
Condition |
unit |
Containing 20% TPU |
Melt Index |
D1238 |
- |
g/10min |
- |
Specific Gravity |
D792 |
- |
- |
1.36 |
Water Absorption |
D570 |
23°C, Water, 24h |
% |
1.3 |
Poisson's Ratio |
D638 |
23°C |
- |
- |
Molding Shrinkage(1/8') |
D955 |
- |
% |
1.7~2.0 |
Melting Point |
D1525 |
- |
°C |
- |
Heat Deflection Temperature |
D648 |
4.6kgf/cm² |
°C |
135 |
18.6kgf/cm² |
°C |
85 |
||
Vicat Softening Temperature |
D1525 |
- |
- |
- |
Coefficient of Linear Thermal Expansion |
D696 |
- |
X10^-4 1/K |
13 |
Tensile Strength |
D638 |
23°C |
Kg/cm^2 |
420 |
Tensile Elongation |
D638 |
23°C |
% |
150 |
Flexural Strength |
D790 |
23°C |
Kg/cm^2 |
550 |
Flexural Modulus |
D790 |
23°C |
Kg/cm^2 |
15000 |
Izod Impact Strength |
D256 |
Notched |
Kg.cm/cm |
18 |
Rockwell Hardness |
D785 |
M-scale |
- |
60 |
Flammability |
UL94 |
- |
- |
HB |
Dielectric Constant |
D150 |
10^6Hz |
- |
- |
Dielectric Dissipation Factor |
D150 |
10^6Hz |
- |
- |
Volume Resistivity |
D257 |
- |
Ω·CM |
1*10^15 |
Dielectric Strength |
D149 |
- |
KV/MM |
- |