PP- Function Added
KOPLA PP |
SORT |
PP FUNCTION ADDED |
||||||
NEW |
KPG1020F |
KPT1020F |
KPU2015F |
KPP1000ST |
KPX1011 |
|||
OLD |
- |
- |
- |
- |
- |
|||
Properties |
Test Method (ASTM) |
Condition |
unit |
FR |
SEE Throughness |
MF & LW Lightweight |
||
GF(H) |
MF(H) |
MF & ST |
||||||
Specific Gravity |
D792 |
- |
- |
1.34 |
1.12 |
1.08 |
0.91 |
0.93 |
Water Absorption |
D570 |
23°C, Water, 24h |
% |
- |
- |
- |
- |
- |
Poisson's Ratio |
D638 |
23°C |
- |
- |
- |
- |
- |
- |
Molding Shrinkage(1/8') |
D955 |
Flow |
% |
0.4-0.6 |
0.9-1.4 |
1.6-1.8 |
1.3-1.5 |
0.9-1.4 |
Xflow |
% |
- |
- |
- |
- |
- |
||
Melting Point |
DSC Method |
- |
°C |
163 |
163 |
163 |
163 |
163 |
Heat Deflection Temperature |
D648 |
4.6kgf/cm² |
°C |
155 |
140 |
115 |
135 |
135 |
18.6kgf/cm² |
°C |
145 |
92 |
- |
- |
- |
||
Coefficient of Linear Thermal Expansion |
D696 |
- |
X10-5l/K |
- |
- |
- |
- |
- |
Tensile Strength |
D638 |
23°C |
Mpa |
65 |
35 |
25 |
40 |
32 |
Tensile Modulus |
D639 |
23°C |
3800 |
2900 |
1800 |
1800 |
2700 |
|
Tensile Elongation |
D638 |
23°C |
% |
8 |
45 |
20 |
80 |
35 |
Flexural Strength |
D790 |
23°C |
Mpa |
90 |
55 |
35 |
42 |
50 |
Flexural Modulus |
D790 |
23°C |
Mpa |
3300 |
2500 |
1500 |
1500 |
2400 |
Izod Impact Strength |
D256 |
Notched |
Mpa |
7 |
4 |
7 |
5 |
5 |
Rockwell Hardness |
D785 |
R-scale |
kJ/M^2 |
110 |
105 |
85 |
105 |
105 |
Flammability |
UL94 |
- |
- |
V-1 |
V-1 |
V-2 |
HB |
HB |
Dielectric Constant |
D150 |
10^6Hz |
- |
- |
- |
- |
- |
- |
Dielectric Dissipation Factor |
D150 |
10^6Hz |
- |
- |
- |
- |
- |
- |
Volume Resistivity |
D257 |
- |
Ω·CM |
- |
- |
- |
- |
- |
Dielectric Strength |
D149 |
- |
KV/mm m |
- |
- |
- |
- |
- |