PBT و PET- مقاوم به شعله
KOPLA PBT &PET |
SORT |
PBT/ PET FLAME RETARDANT GRADE |
|||||||
NEW |
KBP1000F |
KBG1010F |
KBG1015F |
KBG1020F |
KBG1030F |
KEG1030F |
|||
OLD |
UF140 |
UR14030 |
UR14045 |
UR14060 |
UR14090 |
UR17090 |
|||
Properties |
Test Method (ASTM) |
Condition |
unit |
FR(NH) |
GF & FR (H) |
||||
PBT |
PBT |
PET |
|||||||
Specific Gravity |
D792 |
- |
- |
1.42 |
1.5 |
1.52 |
1.55 |
1.62 |
1.67 |
Water Absorption |
D570 |
23°C, Water, 24h |
% |
0.1 |
0.1 |
0.1 |
0.1 |
0.1 |
0.05 |
Poisson's Ratio |
D638 |
23°C |
- |
- |
- |
- |
- |
- |
- |
Molding Shrinkage(1/8') |
D955 |
Flow |
% |
1.2-2.0 |
0.8-1.8 |
0.4-1.0 |
0.3-1.0 |
0.3-1.0 |
0.1-0.3 |
Xflow |
% |
- |
- |
- |
- |
- |
- |
||
Melting Point |
DSC Method |
- |
°C |
225 |
225 |
225 |
225 |
225 |
225 |
Heat Deflection Temperature |
D648 |
4.6kgf/cm² |
°C |
165 |
210 |
210 |
215 |
215 |
240 |
18.6kgf/cm² |
°C |
62 |
200 |
200 |
210 |
210 |
220 |
||
Coefficient of Linear Thermal Expansion |
D696 |
- |
X10-5l/K |
7 |
4 |
4 |
4 |
4 |
3 |
Tensile Strength |
D638 |
23°C |
Mpa |
52 |
80 |
98 |
115 |
130 |
135 |
Tensile Modulus |
D639 |
23°C |
2600 |
5100 |
6600 |
8200 |
9700 |
11500 |
|
Tensile Elongation |
D638 |
23°C |
% |
>50 |
4 |
4 |
4 |
3 |
4.5 |
Flexural Strength |
D790 |
23°C |
Mpa |
73 |
135 |
152 |
165 |
190 |
230 |
Flexural Modulus |
D790 |
23°C |
Mpa |
2300 |
4500 |
5800 |
7200 |
8500 |
10000 |
Izod Impact Strength |
D256 |
Notched |
Mpa |
6 |
5 |
5.4 |
6.5 |
8.5 |
7.5 |
Rockwell Hardness |
D785 |
R-scale |
kJ/M^2 |
120 |
120 |
120 |
120 |
120 |
120 |
Flammability |
UL94 |
- |
- |
V-0 |
V-0 |
V-0 |
V-0 |
V-0 |
V-0 |
Dielectric Constant |
D150 |
10^6Hz |
- |
3.2 |
3.4 |
3.5 |
3.6 |
3.7 |
3.7 |
Dielectric Dissipation Factor |
D150 |
10^6Hz |
- |
0.01 |
0.01 |
0.01 |
0.01 |
0.01 |
0.01 |
Volume Resistivity |
D257 |
- |
Ω·CM |
1*10^13 |
1*10^17 |
1*10^17 |
1*10^17 |
1*10^17 |
1.8*10 |
Dielectric Strength |
D149 |
- |
KV/mm m |
20 |
23 |
23 |
23 |
23 |
23 |