KOPLA PA6

SORT

ALLOY AND IMPACT MODIFIED GRADE

NEW

KNE1005

KNE1010

KNE1015

KNE1020

KNE1030

KRE1110

OLD

-

H100N

-

USN16060

USN16090

WH1002

Properties

Test Method (ASTM)

Condition

unit

Impact Modified Grade

PA6/ABS Alloy

Specific Gravity

D792

-

-

1.11

1.09

1.08

1.06

1.04

1.06

Water Absorption

D570

23°C, Water, 24h

%

1.3

1.3

1.2

1.2

1.2

1.2

Poisson's Ratio

D638

23°C

-

0.37

0.37

0.37

0.37

0.37

0.37

Molding Shrinkage(1/8')

D955

Flow

%

1.2-1.6

1.2-1.6

1.3-1.7

1.3-1.7

1.4-1.8

1.1-1.5

Xflow

%

1.3-1.6

1.3-1.6

1.4-1.7

1.4-1.7

1.5-1.9

1.2-1.5

Melting Point

DSC Method

-

°C

222

222

222

222

222

222

Heat Deflection Temperature

D648

4.6kgf/cm²

°C

180

165

130

120

105

150

18.6kgf/cm²

°C

60

60

60

-

-

-

Coefficient of Linear Thermal Expansion

D696

-

X10^-5 1/K

8

8

8

8

8

6

Tensile Strength

D638

23°C

MPa

68

60

55

50

40

50

Tensile Modulus

D639

23°C

Mpa

2700

2400

2180

1950

1490

2180

Tensile Elongation

D638

23°C

%

150

200

>200

>200

>200

30

Flexural Strength

D790

23°C

Mpa

110

85

80

70

50

70

Flexural Modulus

D790

23°C

Mpa

2350

2100

1900

1700

1300

1900

Izod Impact Strength

D256

Notched

Mpa

17

18

70

NB

NB

15

Rockwell Hardness

D785

R-scale

KJ/M^2

115

115

110

105

100

105

Flammability

UL94

-

-

HB

HB

HB

HB

HB

HB

Dielectric Constant

D150

10^6Hz

-

3.2

3.2

3.2

3.2

3.2

3.2

Dielectric Dissipation Factor

D150

10^6Hz

-

0.02

0.02

0.02

0.02

0.02

0.02

Volume Resistivity

D257

-

Ω·CM

1*10^15

1*10^15

1*10^15

1*10^15

1*10^15

1*10^15

Dielectric Strength

D149

-

KV/MM

20

20

20

20

20

20