PBT و PET- تقویت شده
KOPLA PBT &PET |
SORT |
PBT/PET REINFORCED GRADE |
|||||||
NEW |
KBG1015 |
KBG1020 |
KBG1030 |
KEG1015 |
KEG1020 |
KEG1030 |
|||
OLD |
UG14045 |
UG14060 |
UG14090 |
UG17045 |
UG17060 |
UG17090 |
|||
Properties |
Test Method (ASTM) |
Condition |
unit |
GF Reinforced |
|||||
PBT |
PET |
||||||||
Specific Gravity |
D792 |
- |
- |
1.41 |
1.44 |
1.52 |
1.45 |
1.5 |
1.61 |
Water Absorption |
D570 |
23°C, Water, 24h |
% |
0.1 |
0.1 |
0.1 |
0.1 |
0.1 |
0.1 |
Poisson's Ratio |
D638 |
23°C |
- |
- |
- |
- |
- |
- |
- |
Molding Shrinkage(1/8') |
D955 |
Flow |
% |
0.4-1.1 |
0.4-1.1 |
03-0.9 |
0.2-0.5 |
0.2-0.5 |
0.2-0.5 |
Xflow |
% |
- |
- |
- |
- |
- |
- |
||
Melting Point |
DSC Method |
- |
°C |
225 |
225 |
225 |
225 |
225 |
225 |
Heat Deflection Temperature |
D648 |
4.6kgf/cm² |
°C |
210 |
210 |
215 |
235 |
240 |
240 |
18.6kgf/cm² |
°C |
200 |
200 |
210 |
185 |
200 |
220 |
||
Coefficient of Linear Thermal Expansion |
D696 |
- |
X10-5l/K |
4 |
4 |
4 |
4 |
4 |
4 |
Tensile Strength |
D638 |
23°C |
Mpa |
95 |
110 |
120 |
100 |
110 |
120 |
Tensile Modulus |
D639 |
23°C |
5700 |
7300 |
8900 |
6300 |
7400 |
9200 |
|
Tensile Elongation |
D638 |
23°C |
% |
4 |
4 |
3 |
6 |
6 |
6 |
Flexural Strength |
D790 |
23°C |
Mpa |
150 |
160 |
180 |
155 |
160 |
200 |
Flexural Modulus |
D790 |
23°C |
Mpa |
5000 |
6400 |
7800 |
5500 |
6500 |
8000 |
Izod Impact Strength |
D256 |
Notched |
Mpa |
5 |
6 |
7.5 |
3.5 |
6 |
6.2 |
Rockwell Hardness |
D785 |
R-scale |
kJ/M^2 |
120 |
120 |
120 |
115 |
115 |
115 |
Flammability |
UL94 |
- |
- |
HB |
HB |
HB |
HB |
HB |
HB |
Dielectric Constant |
D150 |
10^6Hz |
- |
3.2 |
3.2 |
3.2 |
3.7 |
3.7 |
3.8 |
Dielectric Dissipation Factor |
D150 |
10^6Hz |
- |
0.01 |
0.01 |
0.01 |
0.01 |
0.01 |
0.01 |
Volume Resistivity |
D257 |
- |
Ω·CM |
1*10^17 |
1*10^16 |
1*10^16 |
1.5*10 |
1.5*10 |
1.5*10 |
Dielectric Strength |
D149 |
- |
KV/mm m |
23 |
23 |
23 |
23 |
23 |
23 |