KOPLA PA6

SORT

FLAME RETARDANT GRADE

NEW

KNP1000F

KNG1020F

KNG1020

KNG1025F

KNG1030F

OLD

UF160

UR16040

UR16060

-

UR16090

Properties

Test Method (ASTM)

Condition

unit

FR (NH)

GF & FR(H)

Specific Gravity

D792

-

-

1.15

1.45

1.5

1.54

1.58

Water Absorption

D570

23°C, Water, 24h

%

1.2

1.1

1.1

1.1

1.1

Poisson's Ratio

D638

23°C

-

0.36

0.35

0.35

0.35

0.35

Molding Shrinkage(1/8')

D955

Flow

%

0.9-1.3

0.6-0.9

0.4-0.7

0.3-0.6

0.2-0.5

Xflow

%

1.1-1.6

0.7-1.1

0.6-0.9

0.5-0.9

0.4-0.8

Melting Point

DSC Method

-

°C

222

222

222

222

222

Heat Deflection Temperature

D648

4.6kgf/cm²

°C

190

200

205

205

215

18.6kgf/cm²

°C

60

190

190

195

200

Coefficient of Linear Thermal Expansion

D696

-

X10^-5 1/K

8

5

5

5

5

Tensile Strength

D638

23°C

MPa

80

120

135

150

155

Tensile Modulus

D639

23°C

Mpa

3450

5170

6670

8600

10400

Tensile Elongation

D638

23°C

%

20

3

3

3

3

Flexural Strength

D790

23°C

Mpa

115

155

185

210

210

Flexural Modulus

D790

23°C

Mpa

3000

4500

5800

7500

9100

Izod Impact Strength

D256

Notched

Mpa

5

5

7

10

13

Rockwell Hardness

D785

R-scale

KJ/M^2

120

120

120

120

120

Flammability

UL94

-

-

V-0

V-0

V-0

V-0

V-0

Dielectric Constant

D150

10^6Hz

-

3.4

3.5

3.5

3.5

3.5

Dielectric Dissipation Factor

D150

10^6Hz

-

0.02

0.02

0.02

0.02

0.02

Volume Resistivity

D257

-

Ω·CM

1*10^15

1*10^15

1*10^15

1*10^15

1*10^15

Dielectric Strength

D149

-

KV/MM

20

22

22

22

22