Polyamide 6-high impact resistant and alloys
KOPLA PA6 |
SORT |
ALLOY AND IMPACT MODIFIED GRADE |
|||||||
NEW |
KNE1005 |
KNE1010 |
KNE1015 |
KNE1020 |
KNE1030 |
KRE1110 |
|||
OLD |
- |
H100N |
- |
USN16060 |
USN16090 |
WH1002 |
|||
Properties |
Test Method (ASTM) |
Condition |
unit |
Impact Modified Grade |
PA6/ABS Alloy |
||||
Specific Gravity |
D792 |
- |
- |
1.11 |
1.09 |
1.08 |
1.06 |
1.04 |
1.06 |
Water Absorption |
D570 |
23°C, Water, 24h |
% |
1.3 |
1.3 |
1.2 |
1.2 |
1.2 |
1.2 |
Poisson's Ratio |
D638 |
23°C |
- |
0.37 |
0.37 |
0.37 |
0.37 |
0.37 |
0.37 |
Molding Shrinkage(1/8') |
D955 |
Flow |
% |
1.2-1.6 |
1.2-1.6 |
1.3-1.7 |
1.3-1.7 |
1.4-1.8 |
1.1-1.5 |
Xflow |
% |
1.3-1.6 |
1.3-1.6 |
1.4-1.7 |
1.4-1.7 |
1.5-1.9 |
1.2-1.5 |
||
Melting Point |
DSC Method |
- |
°C |
222 |
222 |
222 |
222 |
222 |
222 |
Heat Deflection Temperature |
D648 |
4.6kgf/cm² |
°C |
180 |
165 |
130 |
120 |
105 |
150 |
18.6kgf/cm² |
°C |
60 |
60 |
60 |
- |
- |
- |
||
Coefficient of Linear Thermal Expansion |
D696 |
- |
X10^-5 1/K |
8 |
8 |
8 |
8 |
8 |
6 |
Tensile Strength |
D638 |
23°C |
MPa |
68 |
60 |
55 |
50 |
40 |
50 |
Tensile Modulus |
D639 |
23°C |
Mpa |
2700 |
2400 |
2180 |
1950 |
1490 |
2180 |
Tensile Elongation |
D638 |
23°C |
% |
150 |
200 |
>200 |
>200 |
>200 |
30 |
Flexural Strength |
D790 |
23°C |
Mpa |
110 |
85 |
80 |
70 |
50 |
70 |
Flexural Modulus |
D790 |
23°C |
Mpa |
2350 |
2100 |
1900 |
1700 |
1300 |
1900 |
Izod Impact Strength |
D256 |
Notched |
Mpa |
17 |
18 |
70 |
NB |
NB |
15 |
Rockwell Hardness |
D785 |
R-scale |
KJ/M^2 |
115 |
115 |
110 |
105 |
100 |
105 |
Flammability |
UL94 |
- |
- |
HB |
HB |
HB |
HB |
HB |
HB |
Dielectric Constant |
D150 |
10^6Hz |
- |
3.2 |
3.2 |
3.2 |
3.2 |
3.2 |
3.2 |
Dielectric Dissipation Factor |
D150 |
10^6Hz |
- |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
Volume Resistivity |
D257 |
- |
Ω·CM |
1*10^15 |
1*10^15 |
1*10^15 |
1*10^15 |
1*10^15 |
1*10^15 |
Dielectric Strength |
D149 |
- |
KV/MM |
20 |
20 |
20 |
20 |
20 |
20 |