پلی کربنات
Honam PC |
SORT |
PMMA |
|||
Name |
PC-1100 |
PC-1100U |
|||
Properties |
Test Method (ASTM) |
Condition |
unit |
SHEET EXTRUSION & INJECTION GRADE |
|
- |
UV stabilized |
||||
Melt Flow Index, |
D1238 |
300℃, 1.2kg |
g/10min |
10 |
10 |
Specific Gravity |
D792 |
- |
- |
1.2 |
1.2 |
Water Absorption |
D570 |
23°C, Water, 24h |
% |
0.02 |
0.02 |
Molding Shrinkage(1/8') |
D955 |
- |
% |
0.5~0.7 |
0.5~0.7 |
Melting Point |
D1525 |
- |
°C |
290 ~ 310 |
290 ~ 310 |
Heat Deflection Temperature |
D648 |
4.6kgf/cm² |
°C |
143 |
143 |
18.6kgf/cm² |
°C |
132 |
132 |
||
Vicat Softening Temperature |
D1525 |
Rate B/50 |
°C |
150 |
150 |
Tensile Strength |
D638 |
yield, 50mm/min |
kgf/cm^2 |
630 |
630 |
Tensile Elongation |
D638 |
break, 50mm/min |
% |
>100 |
>100 |
Flexural Strength |
D790 |
yield, 10mm/min |
kgf/cm^2 |
920 |
920 |
Flexural Modulus |
D790 |
10mm/min |
kgf/cm^2 |
24000 |
24000 |
Izod Impact Strength |
D256 |
notched, 23 ℃, 1/8” |
kg∙cm/cm |
80 |
80 |
D257 |
notched, 23 ℃, 1/4” |
kg∙cm/cm |
- |
- |
|
Light Transmittance |
D1003 |
- |
% |
89 |
89 |
Haze |
D1003 |
- |
% |
< 0.8 |
< 0.8 |
Refractive Index |
D542 |
- |
- |
1.585 |
1.585 |