PBT و PET- آلیاژ
KOPLA PBT &PET |
SORT |
PBT/PET ALLOY |
|||
NEW |
KUG1030W |
KUG1150W |
|||
OLD |
- |
- |
|||
Properties |
Test Method (ASTM) |
Condition |
unit |
PBT/PET ALLOY GF &WR |
|
Specific Gravity |
D792 |
- |
- |
1.56 |
1.7 |
Water Absorption |
D570 |
23°C, Water, 24h |
% |
0.1 |
0.1 |
Poisson's Ratio |
D638 |
23°C |
- |
- |
- |
Molding Shrinkage(1/8') |
D955 |
Flow |
% |
0.2-0.5 |
0.2-0.5 |
Xflow |
% |
- |
- |
||
Melting Point |
DSC Method |
- |
°C |
225/255 |
225/255 |
Heat Deflection Temperature |
D648 |
4.6kgf/cm² |
°C |
215 |
240 |
18.6kgf/cm² |
°C |
210 |
225 |
||
Coefficient of Linear Thermal Expansion |
D696 |
- |
X10-5l/K |
4 |
4 |
Tensile Strength |
D638 |
23°C |
Mpa |
120 |
145 |
Tensile Modulus |
D639 |
23°C |
8900 |
10900 |
|
Tensile Elongation |
D638 |
23°C |
% |
3 |
3 |
Flexural Strength |
D790 |
23°C |
Mpa |
180 |
230 |
Flexural Modulus |
D790 |
23°C |
Mpa |
7800 |
9500 |
Izod Impact Strength |
D256 |
Notched |
Mpa |
7.5 |
7.5 |
Rockwell Hardness |
D785 |
R-scale |
kJ/M^2 |
120 |
120 |
Flammability |
UL94 |
- |
- |
HB |
HB |
Dielectric Constant |
D150 |
10^6Hz |
- |
3.2 |
3.8 |
Dielectric Dissipation Factor |
D150 |
10^6Hz |
- |
0.01 |
0.01 |
Volume Resistivity |
D257 |
- |
Ω·CM |
1*10^16 |
1*10 |
Dielectric Strength |
D149 |
- |
KV/mm m |
23 |
23 |