PBT- ساده
KOPLA PBT &PET |
SORT |
PBT UNFILLED GRADE |
|||
NEW |
KBP1000 |
KBP1100 |
|||
OLD |
U140L |
U140H |
|||
Properties |
Test Method (ASTM) |
Condition |
unit |
Injection Grade/PBT |
|
Low Viscosity |
High viscosity |
||||
Specific Gravity |
D792 |
- |
- |
1.3 |
1.31 |
Water Absorption |
D570 |
23°C, Water, 24h |
% |
0.1 |
0.1 |
Poisson's Ratio |
D638 |
23°C |
- |
- |
- |
Molding Shrinkage(1/8') |
D955 |
Flow |
% |
2.0-2.1 |
1.2-2.0 |
Xflow |
% |
- |
- |
||
Melting Point |
DSC Method |
- |
°C |
225 |
225 |
Heat Deflection Temperature |
D648 |
4.6kgf/cm² |
°C |
174 |
154 |
18.6kgf/cm² |
°C |
61 |
57 |
||
Coefficient of Linear Thermal Expansion |
D696 |
- |
X10-5l/K |
8 |
8 |
Tensile Strength |
D638 |
23°C |
Mpa |
59 |
55 |
Tensile Modulus |
D639 |
23°C |
2800 |
2600 |
|
Tensile Elongation |
D638 |
23°C |
% |
100 |
>100 |
Flexural Strength |
D790 |
23°C |
Mpa |
86 |
85 |
Flexural Modulus |
D790 |
23°C |
Mpa |
2500 |
2300 |
Izod Impact Strength |
D256 |
Notched |
Mpa |
3.3 |
3.5 |
Rockwell Hardness |
D785 |
R-scale |
kJ/M^2 |
120 |
120 |
Flammability |
UL94 |
- |
- |
HB |
HB |
Dielectric Constant |
D150 |
10^6Hz |
- |
3.1 |
3.1 |
Dielectric Dissipation Factor |
D150 |
10^6Hz |
- |
0.02 |
0.02 |
Volume Resistivity |
D257 |
- |
Ω·CM |
1*10^17 |
1*10^17 |
Dielectric Strength |
D149 |
- |
KV/mm m |
23 |
23 |