pp- تقویت شده
KOPLA PP |
SORT |
PP FILLLED & REINFORCED GRADE |
|||||||
NEW |
KPG1010 |
KPG1020 |
KPG1030 |
KPG1035M |
KPG1040 |
KPG1045 |
|||
OLD |
UG13030 |
UG13060 |
UG13090 |
- |
UG13020 |
UG13005 |
|||
Properties |
Test Method (ASTM) |
Condition |
unit |
GF Reinforced |
|||||
Specific Gravity |
D792 |
- |
- |
0.99 |
1.03 |
1.14 |
1.16 |
1.21 |
1.23 |
Water Absorption |
D570 |
23°C, Water, 24h |
% |
- |
- |
- |
- |
- |
- |
Poisson's Ratio |
D638 |
23°C |
- |
- |
- |
- |
- |
- |
- |
Molding Shrinkage(1/8') |
D955 |
Flow |
% |
0.4-0.6 |
0.4-0.6 |
0.3-0.5 |
0.2-0.3 |
0.2-0.3 |
0.2-0.25 |
Xflow |
% |
- |
- |
- |
- |
- |
- |
||
Melting Point |
DSC Method |
- |
°C |
163 |
163 |
163 |
163 |
163 |
163 |
Heat Deflection Temperature |
D648 |
4.6kgf/cm² |
°C |
150 |
155 |
160 |
160 |
160 |
160 |
18.6kgf/cm² |
°C |
140 |
154 |
150 |
155 |
155 |
155 |
||
Coefficient of Linear Thermal Expansion |
D696 |
- |
X10-5l/K |
5 |
4.5 |
4 |
3.5 |
3 |
2.5 |
Tensile Strength |
D638 |
23°C |
Mpa |
50 |
75 |
87 |
90 |
110 |
115 |
Tensile Modulus |
D639 |
23°C |
2300 |
4000 |
6400 |
6900 |
8000 |
9700 |
|
Tensile Elongation |
D638 |
23°C |
% |
10 |
10 |
6 |
6 |
4 |
4 |
Flexural Strength |
D790 |
23°C |
Mpa |
70 |
100 |
120 |
120 |
160 |
170 |
Flexural Modulus |
D790 |
23°C |
Mpa |
2000 |
3500 |
5600 |
6000 |
7000 |
8500 |
Izod Impact Strength |
D256 |
Notched |
Mpa |
5 |
7 |
10 |
18 |
18 |
19 |
Rockwell Hardness |
D785 |
R-scale |
kJ/M^2 |
105 |
105 |
110 |
110 |
110 |
115 |
Flammability |
UL94 |
- |
- |
HB |
HB |
HB |
HB |
HB |
HB |
Dielectric Constant |
D150 |
10^6Hz |
- |
- |
- |
- |
- |
- |
- |
Dielectric Dissipation Factor |
D150 |
10^6Hz |
- |
- |
- |
- |
- |
- |
- |
Volume Resistivity |
D257 |
- |
Ω·CM |
- |
- |
- |
- |
- |
- |
Dielectric Strength |
D149 |
- |
KV/mm m |
- |
- |
- |
- |
- |
- |
KOPLA PP |
SORT |
PP FILLLED & REINFORCED GRADE |
||||||||
NEW |
KPR1031 |
KPR1071 |
KPR1166 |
KPT1010 |
KPT1020 |
KPT1030 |
KPT1040 |
|||
OLD |
- |
- |
- |
UT13030 |
UT13060 |
UT13090 |
- |
|||
Properties |
Test Method (ASTM) |
Condition |
unit |
GF & ST |
MF Milled |
|||||
Specific Gravity |
D792 |
- |
- |
1.12 |
1.06 |
1 |
1 |
1.06 |
1.1 |
1.2 |
Water Absorption |
D570 |
23°C, Water, 24h |
% |
- |
- |
- |
- |
- |
- |
- |
Poisson's Ratio |
D638 |
23°C |
- |
- |
- |
- |
- |
- |
- |
- |
Molding Shrinkage(1/8') |
D955 |
Flow |
% |
0.3-0.5 |
0.3-0.6 |
0.8-1.2 |
1.1-1.5 |
0.9-1.4 |
0.7-1.2 |
0.6-1.1 |
Xflow |
% |
- |
- |
- |
- |
- |
- |
- |
||
Melting Point |
DSC Method |
- |
°C |
163 |
163 |
163 |
163 |
163 |
163 |
163 |
Heat Deflection Temperature |
D648 |
4.6kgf/cm² |
°C |
155 |
150 |
127 |
130 |
140 |
140 |
140 |
18.6kgf/cm² |
°C |
145 |
140 |
127 |
73 |
92 |
95 |
110 |
||
Coefficient of Linear Thermal Expansion |
D696 |
- |
X10-5l/K |
- |
- |
- |
7 |
7 |
7 |
7 |
Tensile Strength |
D638 |
23°C |
Mpa |
80 |
70 |
26 |
35 |
37 |
35 |
34 |
Tensile Modulus |
D639 |
23°C |
5100 |
4200 |
1800 |
2100 |
3200 |
4000 |
5000 |
|
Tensile Elongation |
D638 |
23°C |
% |
4 |
6 |
>50 |
60 |
35 |
20 |
10 |
Flexural Strength |
D790 |
23°C |
Mpa |
110 |
100 |
38 |
43 |
49 |
56 |
57 |
Flexural Modulus |
D790 |
23°C |
Mpa |
4500 |
3700 |
1600 |
1900 |
2800 |
3500 |
4400 |
Izod Impact Strength |
D256 |
Notched |
Mpa |
13 |
20 |
8 |
5 |
5 |
3 |
2.5 |
Rockwell Hardness |
D785 |
R-scale |
kJ/M^2 |
110 |
105 |
8.5 |
92 |
95 |
95 |
95 |
Flammability |
UL94 |
- |
- |
HB |
HB |
HB |
HB |
HB |
HB |
HB |
Dielectric Constant |
D150 |
10^6Hz |
- |
- |
- |
- |
- |
- |
- |
- |
Dielectric Dissipation Factor |
D150 |
10^6Hz |
- |
- |
- |
- |
- |
- |
- |
- |
Volume Resistivity |
D257 |
- |
Ω·CM |
- |
- |
- |
- |
- |
- |
- |
Dielectric Strength |
D149 |
- |
KV/mm m |
- |
- |
- |
- |
- |
- |
- |
KOPLA PP |
SORT |
PP FILLLED & REINFORCED GRADE |
|||||||
NEW |
KPU1062 |
KPU1032 |
KPX1062 |
KPX1076 |
KPX1067 |
KPX1035 |
|||
OLD |
- |
- |
UG13045M21 |
- |
UG13045M25 |
UG13090M5 |
|||
Properties |
Test Method (ASTM) |
Condition |
unit |
MF & ST |
GF & MF |
||||
Specific Gravity |
D792 |
- |
- |
1.06 |
1.14 |
1.19 |
1.2 |
1.24 |
1.25 |
Water Absorption |
D570 |
23°C, Water, 24h |
% |
- |
- |
- |
- |
- |
- |
Poisson's Ratio |
D638 |
23°C |
- |
- |
- |
- |
- |
- |
- |
Molding Shrinkage(1/8') |
D955 |
Flow |
% |
0.8-1.0 |
0.8-1.0 |
0.4-0.6 |
0.2-0.4 |
0.3-0.5 |
0.3-0.5 |
Xflow |
% |
- |
- |
- |
- |
- |
- |
||
Melting Point |
DSC Method |
- |
°C |
163 |
163 |
163 |
163 |
163 |
163 |
Heat Deflection Temperature |
D648 |
4.6kgf/cm² |
°C |
132 |
132 |
148 |
155 |
150 |
155 |
18.6kgf/cm² |
°C |
- |
- |
145 |
150 |
147 |
150 |
||
Coefficient of Linear Thermal Expansion |
D696 |
- |
X10-5l/K |
- |
- |
- |
- |
- |
- |
Tensile Strength |
D638 |
23°C |
Mpa |
25 |
25 |
75 |
87 |
70 |
95 |
Tensile Modulus |
D639 |
23°C |
2700 |
3100 |
6000 |
8200 |
5300 |
6300 |
|
Tensile Elongation |
D638 |
23°C |
% |
95 |
30 |
3 |
5 |
3 |
4 |
Flexural Strength |
D790 |
23°C |
Mpa |
36 |
40 |
110 |
130 |
110 |
130 |
Flexural Modulus |
D790 |
23°C |
Mpa |
2400 |
2700 |
5200 |
7200 |
4600 |
5500 |
Izod Impact Strength |
D256 |
Notched |
Mpa |
30 |
15 |
8 |
10 |
8 |
15 |
Rockwell Hardness |
D785 |
R-scale |
kJ/M^2 |
90 |
92 |
105 |
105 |
105 |
110 |
Flammability |
UL94 |
- |
- |
HB |
HB |
HB |
HB |
HB |
HB |
Dielectric Constant |
D150 |
10^6Hz |
- |
- |
- |
- |
- |
- |
- |
Dielectric Dissipation Factor |
D150 |
10^6Hz |
- |
- |
- |
- |
- |
- |
- |
Volume Resistivity |
D257 |
- |
Ω·CM |
- |
- |
- |
- |
- |
- |
Dielectric Strength |
D149 |
- |
KV/mm m |
- |
- |
- |
- |
- |
- |