pp- تقویت شده

KOPLA PP

SORT

PP FILLLED & REINFORCED GRADE

NEW

KPG1010

KPG1020

KPG1030

KPG1035M

KPG1040

KPG1045

OLD

UG13030

UG13060

UG13090

-

UG13020

UG13005

Properties

Test Method (ASTM)

Condition

unit

GF Reinforced

Specific Gravity

D792

-

-

0.99

1.03

1.14

1.16

1.21

1.23

Water Absorption

D570

23°C, Water, 24h

%

-

-

-

-

-

-

Poisson's Ratio

D638

23°C

-

-

-

-

-

-

-

Molding Shrinkage(1/8')

D955

Flow

%

0.4-0.6

0.4-0.6

0.3-0.5

0.2-0.3

0.2-0.3

0.2-0.25

Xflow

%

-

-

-

-

-

-

Melting Point

DSC Method

-

°C

163

163

163

163

163

163

Heat Deflection Temperature

D648

4.6kgf/cm²

°C

150

155

160

160

160

160

18.6kgf/cm²

°C

140

154

150

155

155

155

Coefficient of Linear Thermal Expansion

D696

-

X10-5l/K

5

4.5

4

3.5

3

2.5

Tensile Strength

D638

23°C

Mpa

50

75

87

90

110

115

Tensile Modulus

D639

23°C

 

2300

4000

6400

6900

8000

9700

Tensile Elongation

D638

23°C

%

10

10

6

6

4

4

Flexural Strength

D790

23°C

Mpa

70

100

120

120

160

170

Flexural Modulus

D790

23°C

Mpa

2000

3500

5600

6000

7000

8500

Izod Impact Strength

D256

Notched

Mpa

5

7

10

18

18

19

Rockwell Hardness

D785

R-scale

kJ/M^2

105

105

110

110

110

115

Flammability

UL94

-

-

HB

HB

HB

HB

HB

HB

Dielectric Constant

D150

10^6Hz

-

-

-

-

-

-

-

Dielectric Dissipation Factor

D150

10^6Hz

-

-

-

-

-

-

-

Volume Resistivity

D257

-

Ω·CM

-

-

-

-

-

-

Dielectric Strength

D149

-

KV/mm m

-

-

-

-

-

-

 

KOPLA PP

SORT

PP FILLLED & REINFORCED GRADE

NEW

KPR1031

KPR1071

KPR1166

KPT1010

KPT1020

KPT1030

KPT1040

OLD

-

-

-

UT13030

UT13060

UT13090

-

Properties

Test Method (ASTM)

Condition

unit

GF & ST

MF Milled

Specific Gravity

D792

-

-

1.12

1.06

1

1

1.06

1.1

1.2

Water Absorption

D570

23°C, Water, 24h

%

-

-

-

-

-

-

-

Poisson's Ratio

D638

23°C

-

-

-

-

-

-

-

-

Molding Shrinkage(1/8')

D955

Flow

%

0.3-0.5

0.3-0.6

0.8-1.2

1.1-1.5

0.9-1.4

0.7-1.2

0.6-1.1

Xflow

%

-

-

-

-

-

-

-

Melting Point

DSC Method

-

°C

163

163

163

163

163

163

163

Heat Deflection Temperature

D648

4.6kgf/cm²

°C

155

150

127

130

140

140

140

18.6kgf/cm²

°C

145

140

127

73

92

95

110

Coefficient of Linear Thermal Expansion

D696

-

X10-5l/K

-

-

-

7

7

7

7

Tensile Strength

D638

23°C

Mpa

80

70

26

35

37

35

34

Tensile Modulus

D639

23°C

 

5100

4200

1800

2100

3200

4000

5000

Tensile Elongation

D638

23°C

%

4

6

>50

60

35

20

10

Flexural Strength

D790

23°C

Mpa

110

100

38

43

49

56

57

Flexural Modulus

D790

23°C

Mpa

4500

3700

1600

1900

2800

3500

4400

Izod Impact Strength

D256

Notched

Mpa

13

20

8

5

5

3

2.5

Rockwell Hardness

D785

R-scale

kJ/M^2

110

105

8.5

92

95

95

95

Flammability

UL94

-

-

HB

HB

HB

HB

HB

HB

HB

Dielectric Constant

D150

10^6Hz

-

-

-

-

-

-

-

-

Dielectric Dissipation Factor

D150

10^6Hz

-

-

-

-

-

-

-

-

Volume Resistivity

D257

-

Ω·CM

-

-

-

-

-

-

-

Dielectric Strength

D149

-

KV/mm m

-

-

-

-

-

-

-

 

KOPLA PP

SORT

PP FILLLED & REINFORCED GRADE

NEW

KPU1062

KPU1032

KPX1062

KPX1076

KPX1067

KPX1035

OLD

-

-

UG13045M21

-

UG13045M25

UG13090M5

Properties

Test Method (ASTM)

Condition

unit

MF & ST

GF & MF

Specific Gravity

D792

-

-

1.06

1.14

1.19

1.2

1.24

1.25

Water Absorption

D570

23°C, Water, 24h

%

-

-

-

-

-

-

Poisson's Ratio

D638

23°C

-

-

-

-

-

-

-

Molding Shrinkage(1/8')

D955

Flow

%

0.8-1.0

0.8-1.0

0.4-0.6

0.2-0.4

0.3-0.5

0.3-0.5

Xflow

%

-

-

-

-

-

-

Melting Point

DSC Method

-

°C

163

163

163

163

163

163

Heat Deflection Temperature

D648

4.6kgf/cm²

°C

132

132

148

155

150

155

18.6kgf/cm²

°C

-

-

145

150

147

150

Coefficient of Linear Thermal Expansion

D696

-

X10-5l/K

-

-

-

-

-

-

Tensile Strength

D638

23°C

Mpa

25

25

75

87

70

95

Tensile Modulus

D639

23°C

 

2700

3100

6000

8200

5300

6300

Tensile Elongation

D638

23°C

%

95

30

3

5

3

4

Flexural Strength

D790

23°C

Mpa

36

40

110

130

110

130

Flexural Modulus

D790

23°C

Mpa

2400

2700

5200

7200

4600

5500

Izod Impact Strength

D256

Notched

Mpa

30

15

8

10

8

15

Rockwell Hardness

D785

R-scale

kJ/M^2

90

92

105

105

105

110

Flammability

UL94

-

-

HB

HB

HB

HB

HB

HB

Dielectric Constant

D150

10^6Hz

-

-

-

-

-

-

-

Dielectric Dissipation Factor

D150

10^6Hz

-

-

-

-

-

-

-

Volume Resistivity

D257

-

Ω·CM

-

-

-

-

-

-

Dielectric Strength

D149

-

KV/mm m

-

-

-

-

-

-

همکاران تجاری

  • 1.jpg
  • 2.jpg
  • 6.jpg
  • 7.jpg
  • 8.jpg
  • 9.jpg

محصولات

  • product 17.jpg
  • product 1.jpg
  • product 6.jpg
  • product 16.jpg
  • product 3.jpg
  • product 2.jpg
  • product 9.jpg
  • product 8.jpg
  • product 15.jpg
  • product 10.jpg
  • product 12.jpg
  • product 4.jpg
  • product 18.jpg
  • product 11.jpg
  • product 7.jpg
  • product 5.jpg
  • product 14.JPG