پلی آمید 66- مقاوم به شعله
|
KOPLA PA66 |
SORT |
FLAME RETARDANT GRADE |
|||||||||
|
NEW |
KDP1000F |
KDG1010F |
KDG1015F |
KDG1025F |
KDG1030F |
KDG1035F |
KDE2060F |
||||
|
OLD |
UF166 |
UR16630 |
UR16645 |
UR16675 |
UR16690 |
- |
- |
||||
|
Properties |
Test Method (ASTM) |
Condition |
unit |
FR (H) |
GF & FR |
ST & FR (NH) |
|||||
|
H FR |
NH FR |
||||||||||
|
Specific Gravity |
D792 |
- |
- |
1.15 |
1.43 |
1.45 |
1.48 |
1.57 |
1.47 |
1.15 |
|
|
Water Absorption |
D570 |
23°C, Water, 24h |
% |
1 |
0.8 |
0.8 |
0.8 |
0.7 |
0.6 |
1.2 |
|
|
Poisson's Ratio |
D638 |
23°C |
- |
0.39 |
0.38 |
0.38 |
0.38 |
0.38 |
0.38 |
0.39 |
|
|
Molding Shrinkage(1/8') |
D955 |
Flow |
% |
1.5-2.0 |
0.5-0.8 |
0.4-0.7 |
0.3-0.6 |
0.3-0.6 |
0.3-0.7 |
1.7-2.6 |
|
|
Xflow |
% |
1.7-2.2 |
0.7-1.0 |
0.7-1.0 |
0.6-0.9 |
0.5-0.8 |
0.5-0.9 |
2.0-2.9 |
|||
|
Melting Point |
DSC Method |
- |
°C |
260 |
260 |
260 |
260 |
260 |
260 |
260 |
|
|
Heat Deflection Temperature |
D648 |
4.6kgf/cm² |
°C |
235 |
235 |
238 |
250 |
250 |
260 |
210 |
|
|
18.6kgf/cm² |
°C |
95 |
217 |
220 |
225 |
225 |
260 |
65 |
|||
|
Coefficient of Linear Thermal Expansion |
D696 |
- |
X10-5l/K |
6.5 |
4 |
3.5 |
3 |
3 |
2.5 |
- |
|
|
Tensile Strength |
D638 |
23°C(RH0/RH50) |
Mpa |
80/40 |
105/80 |
115/85 |
140/100 |
160/110 |
185/140 |
60/42 |
|
|
Tensile Modulus |
D639 |
23°C(RH0/RH50) |
Mpa |
3700/2200 |
5300/4200 |
5900/4600 |
9000/6500 |
9400/7500 |
11000/8500 |
2300/950 |
|
|
Tensile Elongation |
D638 |
23°C(RH0/RH50) |
% |
5/>50 |
3/5 |
4-Feb |
4-Feb |
2/3.5 |
2/3 |
65/80 |
|
|
Flexural Strength |
D790 |
23°C(RH0/RH50) |
Mpa |
105/70 |
155/96 |
160/100 |
215/150 |
230/170 |
250/185 |
95/45 |
|
|
Flexural Modulus |
D790 |
23°C(RH0/RH50) |
Mpa |
3500/2000 |
5000/3800 |
5500/4100 |
7300/5000 |
8900/6800 |
9200/6600 |
2200/900 |
|
|
Izod Impact Strength |
D256 |
Notched(RH0/RH50) |
Mpa |
3/10 |
7/8 |
8/9 |
3/4 |
11/15 |
13/17 |
9/13 |
|
|
Rockwell Hardness |
D785 |
R-scale(RH0/RH50) |
kJ/M^2 |
120/105 |
120/115 |
120/115 |
120/115 |
120/115 |
120/115 |
110/ |
|
|
Flammability |
UL94 |
32MM |
- |
V-0 |
V-0 |
V-0 |
V-0 |
V-0 |
V-0 |
V-2 |
|
|
Dielectric Constant |
D150 |
10^6Hz |
- |
3.6 |
3 |
3 |
3 |
3.3 |
3.7 |
3 |
|
|
Dielectric Dissipation Factor |
D150 |
10^6Hz |
- |
0.02 |
0.02 |
0.02 |
0.02 |
0.01 |
0.02 |
0.02 |
|
|
Volume Resistivity |
D257 |
- |
Ω·CM |
1*10^14 |
1*10^15 |
1*10^15 |
1*10^15 |
1*10^15 |
1*10^15 |
1*10^14 |
|
|
Dielectric Strength |
D149 |
- |
KV/mm m |
34 |
35 |
40 |
40 |
42 |
35 |
32 |
|