KOPLA PA66
|
SORT
|
FILLED & REINFORCED GRADE
|
|
|
NEW
|
KDG1015
|
KDG1020
|
KDG1030
|
KDG1035
|
KDG1040
|
KDG1050
|
KDG1060
|
KUG1330
|
KDG1033R
|
|
|
OLD
|
UGN16645
|
UGN16660
|
UGN16690
|
-
|
UGN16620
|
UGN16600
|
-
|
-
|
-
|
|
|
Properties
|
Test Method (ASTM)
|
Condition
|
unit
|
GF Reinforced
|
|
| |
| |
|
Specific Gravity
|
D792
|
-
|
-
|
1.23
|
1.28
|
1.37
|
1.42
|
1.46
|
1.56
|
1.72
|
1.37
|
1.39
|
|
|
Water Absorption
|
D570
|
23°C, Water, 24h
|
%
|
1.1
|
1
|
0.8
|
0.75
|
0.6
|
0.5
|
0.5
|
0.8
|
0.75
|
|
|
Poisson's Ratio
|
D638
|
23°C
|
-
|
0.38
|
0.38
|
0.38
|
0.38
|
0.38
|
0.38
|
0.38
|
0.38
|
0.38
|
|
|
Molding Shrinkage(1/8')
|
D955
|
Flow
|
%
|
0.6-1.0
|
0.5-0.9
|
0.3-0.7
|
0.3-0.7
|
0.2-0.6
|
0.1-0.5
|
0.1-0.3
|
0.3-0.7
|
0.3-0.7
|
|
|
Xflow
|
%
|
0.9-1.3
|
0.8-1.2
|
0.6-1.0
|
0.5-0.9
|
0.5-0.9
|
0.3-0.7
|
0.2-0.5
|
0.6-1.0
|
0.5-0.9
|
|
|
Melting Point
|
DSC Method
|
-
|
°C
|
260
|
260
|
260
|
260
|
260
|
260
|
260
|
260
|
260
|
|
|
Heat Deflection Temperature
|
D648
|
4.6kgf/cm²
|
°C
|
255
|
255
|
260
|
260
|
260
|
260
|
260
|
260
|
260
|
|
|
18.6kgf/cm²
|
°C
|
240
|
250
|
255
|
260
|
260
|
260
|
260
|
255
|
260
|
|
|
Coefficient of Linear Thermal Expansion
|
D696
|
-
|
X10-5l/K
|
3.5
|
3
|
2.5
|
2.2
|
2
|
1.5
|
1.2
|
2.5
|
2.2
|
|
|
Tensile Strength
|
D638
|
23°C(RH0/RH50)
|
Mpa
|
125/90
|
145/100
|
190/135
|
210/150
|
255/165
|
240/175
|
210/170
|
190/135
|
200/145
|
|
|
Tensile Modulus
|
D639
|
23°C(RH0/RH50)
|
Mpa
|
6200/4300
|
7400/5300
|
10000/7500
|
11400/8700
|
13000/9900
|
16000/12500
|
18000/13000
|
10000/7500
|
11000/8500
|
|
|
Tensile Elongation
|
D638
|
23°C(RH0/RH50)
|
%
|
42102
|
4/5
|
3/4
|
3/4
|
2/3
|
2/2.5
|
1.5/2
|
3/4
|
3/4
|
|
|
Flexural Strength
|
D790
|
23°C(RH0/RH50)
|
Mpa
|
190/155
|
220/165
|
260/175
|
270/195
|
300/210
|
345/250
|
305/250
|
260/175
|
270/190
|
|
|
Flexural Modulus
|
D790
|
23°C(RH0/RH50)
|
Mpa
|
5300/4200
|
6400/4800
|
8200/5900
|
9500/6800
|
10700/7700
|
13000/9300
|
16500/9600
|
8200/5900
|
9500/6500
|
|
|
Izod Impact Strength
|
D256
|
Notched(RH0/RH50)
|
Mpa
|
42165
|
7/13
|
11/16
|
13/18
|
14/18
|
14.5/17
|
17/19
|
11/16
|
13/18
|
|
|
Rockwell Hardness
|
D785
|
R-scale(RH0/RH50)
|
kJ/M^2
|
120/115
|
120/115
|
120/115
|
120/115
|
120/115
|
125/120
|
125/120
|
120/115
|
120/115
|
|
|
Flammability
|
UL94
|
32MM
|
-
|
HB
|
--HB
|
HB
|
HB
|
HB
|
HB
|
HB
|
HB
|
HB
|
|
|
Dielectric Constant
|
D150
|
10^6Hz
|
-
|
3.7
|
3.7
|
3.7
|
3.7
|
3.7
|
3.7
|
3.7
|
3.7
|
3.7
|
|
|
Dielectric Dissipation Factor
|
D150
|
10^6Hz
|
-
|
0.01
|
0.01
|
0.01
|
0.01
|
0.01
|
0.01
|
0.01
|
0.01
|
0.01
|
|
|
Volume Resistivity
|
D257
|
-
|
Ω·CM
|
1*10^15
|
1*10^15
|
1*10^15
|
1*10^15
|
1*10^15
|
1*10^15
|
1*10^15
|
1*10^15
|
1*10^15
|
|
|
Dielectric Strength
|
D149
|
-
|
KV/mm m
|
31
|
32
|
32
|
34
|
35
|
35
|
35
|
32
|
34
|
|
|
| |
|
KOPLA PA66
|
SORT
|
FILLED & REINFORCED GRADE
|
|
|
NEW
|
KDR1020
|
KDR1026
|
KDR1031
|
KDT1020
|
KDT1030
|
KDT1040
|
|
|
OLD
|
-
|
USG166654
|
USG16690
|
UTN16660
|
UTN16690
|
UTN16620
|
|
|
Properties
|
Test Method (ASTM)
|
Condition
|
unit
|
GF & ST
|
MF Filled
|
|
| |
| |
|
Specific Gravity
|
D792
|
-
|
-
|
1.23
|
1.2
|
1.3
|
1.28
|
1.37
|
1.46
|
|
|
Water Absorption
|
D570
|
23°C, Water, 24h
|
%
|
1
|
0.8
|
0.7
|
0.5
|
0.7
|
1
|
|
|
Poisson's Ratio
|
D638
|
23°C
|
-
|
--0.38
|
0.39
|
0.39
|
0.39
|
0.39
|
0.39
|
|
|
Molding Shrinkage(1/8')
|
D955
|
Flow
|
%
|
0.5-0.9
|
0.6-1.0
|
0.4-0.8
|
0.4-0.9
|
0.4-0.8
|
0.4-0.7
|
|
|
Xflow
|
%
|
0.8-1.2
|
0.9-1.3
|
0.7-1.0
|
0.5-1.0
|
0.5-0.9
|
0.5-0.9
|
|
|
Melting Point
|
DSC Method
|
-
|
°C
|
260
|
260
|
260
|
260
|
260
|
260
|
|
|
Heat Deflection Temperature
|
D648
|
4.6kgf/cm²
|
°C
|
255
|
250
|
255
|
245
|
245
|
245
|
|
|
18.6kgf/cm²
|
°C
|
250
|
235
|
250
|
210
|
215
|
220
|
|
|
Coefficient of Linear
Thermal Expansion
|
D696
|
-
|
X10-5l/K
|
-
|
-
|
|
6.5
|
6.2
|
6
|
|
|
Tensile Strength
|
D638
|
23°C(RH0/RH50)
|
Mpa
|
130/95
|
100/85
|
135/100
|
80
|
80
|
95
|
|
|
Tensile Modulus
|
D639
|
23°C(RH0/RH50)
|
Mpa
|
6300/4500
|
5100/3900
|
7500/5500
|
4980
|
5300
|
5600
|
|
|
Tensile Elongation
|
D638
|
23°C(RH0/RH50)
|
%
|
4/8
|
5/8
|
4/6
|
4.5
|
4.5
|
4
|
|
|
Flexural Strength
|
D790
|
23°C(RH0/RH50)
|
Mpa
|
195/160
|
150/120
|
200/160
|
130
|
135
|
145
|
|
|
Flexural Modulus
|
D790
|
23°C(RH0/RH50)
|
Mpa
|
5500/4300
|
4500/3800
|
6500/4900
|
4800
|
5200
|
5500
|
|
|
Izod Impact Strength
|
D256
|
Notched(RH0/RH50)
|
Mpa
|
17/21
|
23/27
|
21/26
|
5.5
|
5
|
5
|
|
|
Rockwell Hardness
|
D785
|
R-scale(RH0/RH50)
|
kJ/M^2
|
120/115
|
120/115
|
120/115
|
120
|
120
|
120
|
|
|
Flammability
|
UL94
|
32MM
|
-
|
HB
|
HB
|
HB
|
HB
|
HB
|
HB
|
|
|
Dielectric Constant
|
D150
|
10^6Hz
|
-
|
3.7
|
3.7
|
3.7
|
3.7
|
3.7
|
3.7
|
|
|
Dielectric Dissipation Factor
|
D150
|
10^6Hz
|
-
|
0.01
|
0.01
|
0.01
|
0.02
|
0.02
|
0.02
|
|
|
Volume Resistivity
|
D257
|
-
|
Ω·CM
|
1*10^15
|
1*10^15
|
1*10^15
|
1*10^14
|
1*10^14
|
1*10^14
|
|
|
Dielectric Strength
|
D149
|
-
|
KV/mm m
|
32
|
32
|
34
|
32
|
32
|
32
|
|
|
| |
|
KOPLA PA66
|
SORT
|
FILLED & REINFORCED GRADE
|
|
|
NEW
|
KDX1083
|
KDX1013
|
KDX1067
|
KDX1065
|
KDU1021
|
|
|
OLD
|
-
|
-
|
UG16645
M25
|
-
|
UST16660M20
|
|
|
Properties
|
Test Method (ASTM)
|
Condition
|
unit
|
GF & MF
|
MF & ST
|
|
| |
| |
|
Specific Gravity
|
D792
|
-
|
-
|
1.46
|
1.45
|
1.47
|
2.06
|
1.25
|
|
|
Water Absorption
|
D570
|
23°C, Water, 24h
|
%
|
1.1
|
1.1
|
1.1
|
1.1
|
0.5
|
|
|
Poisson's Ratio
|
D638
|
23°C
|
-
|
0.38
|
0.38
|
0.38
|
0.38
|
0.39
|
|
|
Molding Shrinkage(1/8')
|
D955
|
Flow
|
%
|
0.3-0.6
|
0.4-0.7
|
0.3-0.6
|
0.2-0.5
|
0.5-1.0
|
|
|
Xflow
|
%
|
0.4-0.7
|
0.5-0.9
|
0.5-0.9
|
0.3-0.6
|
0.8-1.5
|
|
|
Melting Point
|
DSC Method
|
-
|
°C
|
260
|
260
|
260
|
260
|
260
|
|
|
Heat Deflection
Temperature
|
D648
|
4.6kgf/cm²
|
°C
|
255
|
250
|
255
|
250
|
245
|
|
|
18.6kgf/cm²
|
°C
|
235
|
235
|
240
|
2358
|
225
|
|
|
Coefficient of Linear
Thermal Expansion
|
D696
|
-
|
X10-5l/K
|
3.5
|
3.5
|
3.5
|
-
|
-
|
|
|
Tensile Strength
|
D638
|
23°C(RH0/RH50)
|
Mpa
|
115/70
|
120/70
|
140/100
|
100/65
|
65
|
|
|
Tensile Modulus
|
D639
|
23°C(RH0/RH50)
|
Mpa
|
8500/4500
|
8500/4500
|
9000/5500
|
10000/7500
|
3200
|
|
|
Tensile Elongation
|
D638
|
23°C(RH0/RH50)
|
%
|
2/4
|
2/4
|
2.5/5
|
2/3
|
6
|
|
|
Flexural Strength
|
D790
|
23°C(RH0/RH50)
|
Mpa
|
185/105
|
175/100
|
210/120
|
140/90
|
110
|
|
|
Flexural Modulus
|
D790
|
23°C(RH0/RH50)
|
Mpa
|
6800/4200
|
7000/4200
|
8500/5000
|
9000/5300
|
3000
|
|
|
Izod Impact Strength
|
D256
|
Notched(RH0/RH50)
|
Mpa
|
4.5/6
|
6-Apr
|
4/6.5
|
8-Jun
|
10.5
|
|
|
Rockwell Hardness
|
D785
|
R-scale(RH0/RH50)
|
kJ/M^2
|
120/115
|
120/115
|
120/115
|
120/115
|
115
|
|
|
Flammability
|
UL94
|
32MM
|
-
|
HB
|
HB
|
HB
|
HB
|
HB
|
|
|
Dielectric Constant
|
D150
|
10^6Hz
|
-
|
3.7
|
3.7
|
3.7
|
3.7
|
3.7
|
|
|
Dielectric Dissipation
Factor
|
D150
|
10^6Hz
|
-
|
0.02
|
0.02
|
0.02
|
0.02
|
0.02
|
|
|
Volume Resistivity
|
D257
|
-
|
Ω·CM
|
1*10^14
|
1*10^14
|
1*10^14
|
1*10^14
|
1*10^14
|
|
|
Dielectric Strength
|
D149
|
-
|
KV/mm m
|
36
|
36
|
36
|
36
|
32
|
|
|