پلی آمید 6- مقاوم به شعله
KOPLA PA6 |
SORT |
FLAME RETARDANT GRADE |
||||||
NEW |
KNP1000F |
KNG1020F |
KNG1020 |
KNG1025F |
KNG1030F |
|||
OLD |
UF160 |
UR16040 |
UR16060 |
- |
UR16090 |
|||
Properties |
Test Method (ASTM) |
Condition |
unit |
FR (NH) |
GF & FR(H) |
|||
Specific Gravity |
D792 |
- |
- |
1.15 |
1.45 |
1.5 |
1.54 |
1.58 |
Water Absorption |
D570 |
23°C, Water, 24h |
% |
1.2 |
1.1 |
1.1 |
1.1 |
1.1 |
Poisson's Ratio |
D638 |
23°C |
- |
0.36 |
0.35 |
0.35 |
0.35 |
0.35 |
Molding Shrinkage(1/8') |
D955 |
Flow |
% |
0.9-1.3 |
0.6-0.9 |
0.4-0.7 |
0.3-0.6 |
0.2-0.5 |
Xflow |
% |
1.1-1.6 |
0.7-1.1 |
0.6-0.9 |
0.5-0.9 |
0.4-0.8 |
||
Melting Point |
DSC Method |
- |
°C |
222 |
222 |
222 |
222 |
222 |
Heat Deflection Temperature |
D648 |
4.6kgf/cm² |
°C |
190 |
200 |
205 |
205 |
215 |
18.6kgf/cm² |
°C |
60 |
190 |
190 |
195 |
200 |
||
Coefficient of Linear Thermal Expansion |
D696 |
- |
X10^-5 1/K |
8 |
5 |
5 |
5 |
5 |
Tensile Strength |
D638 |
23°C |
MPa |
80 |
120 |
135 |
150 |
155 |
Tensile Modulus |
D639 |
23°C |
Mpa |
3450 |
5170 |
6670 |
8600 |
10400 |
Tensile Elongation |
D638 |
23°C |
% |
20 |
3 |
3 |
3 |
3 |
Flexural Strength |
D790 |
23°C |
Mpa |
115 |
155 |
185 |
210 |
210 |
Flexural Modulus |
D790 |
23°C |
Mpa |
3000 |
4500 |
5800 |
7500 |
9100 |
Izod Impact Strength |
D256 |
Notched |
Mpa |
5 |
5 |
7 |
10 |
13 |
Rockwell Hardness |
D785 |
R-scale |
KJ/M^2 |
120 |
120 |
120 |
120 |
120 |
Flammability |
UL94 |
- |
- |
V-0 |
V-0 |
V-0 |
V-0 |
V-0 |
Dielectric Constant |
D150 |
10^6Hz |
- |
3.4 |
3.5 |
3.5 |
3.5 |
3.5 |
Dielectric Dissipation Factor |
D150 |
10^6Hz |
- |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
Volume Resistivity |
D257 |
- |
Ω·CM |
1*10^15 |
1*10^15 |
1*10^15 |
1*10^15 |
1*10^15 |
Dielectric Strength |
D149 |
- |
KV/MM |
20 |
22 |
22 |
22 |
22 |