پلی آمید 6- تقویت شده
KOPLA PA6 |
SORT |
FILLED & REINFORCED GRADE |
|||||||||
NEW |
KNG1015 |
KNG1020 |
KNG1030 |
KNG1045 |
KNG1050 |
KNG1060 |
KNR1061 |
KNR1031 |
|||
OLD |
UGN16045 |
UGN16060 |
UGN16090 |
UGN16005 |
UGN16000 |
- |
USG16045 |
USG16090 |
|||
Properties |
Test Method (ASTM) |
Condition |
unit |
GF Reinforced |
|||||||
Specific Gravity |
D792 |
- |
- |
1.23 |
1.27 |
1.36 |
1.51 |
1.56 |
1.68 |
1.22 |
1.31 |
Water Absorption |
D570 |
23°C, Water, 24h |
% |
1.15 |
1 |
0.95 |
0.8 |
0.75 |
0.7 |
1.3 |
0.9 |
Poisson's Ratio |
D638 |
23°C |
- |
0.35 |
0.35 |
0.35 |
0.35 |
0.35 |
0.35 |
- |
- |
Molding Shrinkage(1/8') |
D955 |
Flow |
% |
0.7-1.0 |
0.6-0.9 |
0.4-0.7 |
0.1-0.5 |
0.1-0.5 |
0.1-0.3 |
0.7-1.1 |
0.4-0.8 |
Xflow |
% |
0.9-1.2 |
0.7-1.1 |
0.6-0.9 |
0.4-0.8 |
0.3-0.7 |
0.2-0.5 |
0.9-1.3 |
0.6-1.0 |
||
Melting Point |
DSC |
- |
°C |
222 |
222 |
222 |
222 |
222 |
222 |
222 |
222 |
Heat Deflection Temperature |
D648 |
4.6kgf/cm² |
°C |
220 |
220 |
220 |
220 |
220 |
220 |
210 |
210 |
18.6kgf/cm² |
°C |
205 |
205 |
210 |
215 |
215 |
215 |
190 |
200 |
||
Coefficient of Linear Thermal Expansion |
D696 |
- |
X10^-5 1/K |
4.2 |
3.9 |
3.2 |
2 |
1.8 |
1.5 |
- |
- |
Tensile Strength |
D638 |
23°C |
MPa(RH0/RH50) |
120/70 |
145/95 |
170/110 |
215/140 |
225/150 |
230/160 |
100 |
145 |
Tensile Modulus |
D639 |
23°C |
MPa(RH0/RH50) |
6100/2900 |
6600/3800 |
9600/6200 |
13100/7300 |
14600/8600 |
14600/9000 |
5100 |
8300 |
Tensile Elongation |
D638 |
23°C |
%(RH0/RH50) |
4/7 |
3/4 |
3/4 |
2/3 |
2/3 |
2/3 |
6 |
4 |
Flexural Strength |
D790 |
23°C |
MPa(RH0/RH50) |
170/ |
200/150 |
230/170 |
350/210 |
360/270 |
370/280 |
145 |
210 |
Flexural Modulus |
D790 |
23°C |
MPa(RH0/RH50) |
4800/2800 |
5600/3700 |
7900/5500 |
13000/7200 |
14500/8500 |
14900/9200 |
4400 |
7200 |
Izod Impact Strength |
D256 |
Notched |
MPa(RH0/RH50) |
- |
- |
15/24 |
16/29 |
17/29 |
18/29 |
14 |
21 |
Rockwell Hardness |
D785 |
R-scale |
KJ/M^2(RH0/RH50) |
120/115 |
120/115 |
120/115 |
125/115 |
125/115 |
125/115 |
115 |
115 |
Flammability |
UL94 |
- |
- |
HB |
HB |
HB |
HB |
HB |
HB |
HB |
HB |
Dielectric Constant |
D150 |
10^6Hz |
- |
3.8 |
3.8 |
3.8 |
3.8 |
3.8 |
3.8 |
3.8 |
3.8 |
Dielectric Dissipation Factor |
D150 |
10^6Hz |
- |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
Volume Resistivity |
D257 |
- |
Ω·CM |
1*10^15 |
1*10^15 |
1*10^15 |
1*10^15 |
1*10^15 |
1*10^15 |
1*10^15 |
1*10^15 |
Dielectric Strength |
D149 |
- |
KV/MM |
22 |
22 |
22 |
22 |
22 |
22 |
22 |
22 |
KOPLA PA6 |
SORT |
FILLED & REINFORCED GRADE |
|||||||
NEW |
KNT1015 |
KNT1020 |
KNT1030 |
KNT1040 |
KNT1060 |
KNT2040 |
|||
OLD |
- |
UTN16060 |
UTN16090 |
UTN16020 |
UT160180 |
- |
|||
Properties |
Test Method (ASTM) |
Condition |
unit |
MF Filled |
|||||
Specific Gravity |
D792 |
- |
- |
1.21 |
1.25 |
1.38 |
1.45 |
2.05 |
1.46 |
Water Absorption |
D570 |
23°C, Water, 24h |
% |
1.1 |
1.1 |
1.1 |
1.1 |
1.1 |
1.1 |
Poisson's Ratio |
D638 |
23°C |
- |
0.36 |
0.36 |
0.36 |
0.36 |
0.36 |
0.36 |
Molding Shrinkage(1/8') |
D955 |
Flow |
% |
0.6-0.8 |
0.6-0.8 |
0.5-0.8 |
0.5-0.8 |
0.1-0.2 |
0.5-0.8 |
Xflow |
% |
0.7-1.0 |
0.7-1.0 |
0.7-1.1 |
0.7-1.1 |
0.2-0.5 |
0.7-1.1 |
||
Melting Point |
DSC Method |
- |
°C |
222 |
222 |
222 |
222 |
222 |
222 |
Heat Deflection Temperature |
D648 |
4.6kgf/cm² |
°C |
195 |
195 |
200 |
200 |
200 |
200 |
18.6kgf/cm² |
°C |
105 |
105 |
115 |
120 |
120 |
120 |
||
Coefficient of Linear Thermal Expansion |
D696 |
- |
X10^-5 1/K |
6 |
6 |
4 |
4 |
- |
- |
Tensile Strength |
D638 |
23°C |
MPa |
75 |
75 |
75 |
85 |
70 |
50 |
Tensile Modulus |
D639 |
23°C |
MPa |
3900 |
4800 |
6400 |
6900 |
6000 |
4700 |
Tensile Elongation |
D638 |
23°C |
% |
15 |
4 |
3 |
3 |
2 |
30 |
Flexural Strength |
D790 |
23°C |
MPa |
110 |
110 |
120 |
130 |
110 |
90 |
Flexural Modulus |
D790 |
23°C |
MPa |
3400 |
4200 |
5600 |
6000 |
5300 |
4100 |
Izod Impact Strength |
D256 |
Notched |
MPa |
6 |
6 |
6 |
7 |
3 |
6 |
Rockwell Hardness |
D785 |
R-scale |
KJ/M^2 |
120 |
115 |
115 |
115 |
115 |
115 |
Flammability |
UL94 |
- |
- |
HB |
HB |
HB |
HB |
HB |
HB |
Dielectric Constant |
D150 |
10^6Hz |
- |
3.6 |
3.6 |
3.6 |
3.6 |
3.6 |
3.6 |
Dielectric Dissipation Factor |
D150 |
10^6Hz |
- |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
Volume Resistivity |
D257 |
- |
Ω·CM |
1*10^14 |
1*10^14 |
1*10^14 |
1*10^14 |
1*10^14 |
1*10^14 |
Dielectric Strength |
D149 |
- |
KV/MM |
21 |
21 |
21 |
21 |
21 |
21 |
KOPLA PA6 |
SORT |
FILLED & REINFORCED GRADE |
|||||||
NEW |
KNX1014 |
KNX1076 |
KNG1040CW |
KNU1061 |
KNH1012 |
KNU1061 |
|||
OLD |
- |
- |
UGN16045M25 |
- |
- |
||||
Properties |
Test Method (ASTM) |
Condition |
unit |
GF & MF |
GF &GB |
MF & ST |
|||
Specific Gravity |
D792 |
- |
- |
1.27 |
1.47 |
1.46 |
1.48 |
1 |
1.25 |
Water Absorption |
D570 |
23°C, Water, 24h |
% |
1.2 |
1 |
1 |
1 |
1 |
1.1 |
Poisson's Ratio |
D638 |
23°C |
- |
0.35 |
0.35 |
0.35 |
0.35 |
0.35 |
- |
Molding Shrinkage(1/8') |
D955 |
Flow |
% |
0.6-0.8 |
0.1-0.5 |
0.1-0.5 |
0.1-0.5 |
0.4-0.6 |
0.6-0.8 |
Xflow |
% |
0.7-1.0 |
0.4-0.8 |
0.4-0.8 |
0.4-0.8 |
0.6-0.9 |
0.7-1.0 |
||
Melting Point |
DSC Method |
- |
°C |
222 |
222 |
222 |
222 |
222 |
222 |
Heat Deflection Temperature |
D648 |
4.6kgf/cm² |
°C |
210 |
215 |
220 |
215 |
220 |
195 |
18.6kgf/cm² |
°C |
200 |
205 |
210 |
200 |
205 |
105 |
||
Coefficient of Linear Thermal Expansion |
D696 |
- |
X10^-5 1/K |
- |
- |
- |
- |
3 |
- |
Tensile Strength |
D638 |
23°C |
MPa |
100 |
160 |
180 |
130 |
110 |
55 |
Tensile Modulus |
D639 |
23°C |
MPa |
5500 |
10300 |
10500 |
8600 |
5900 |
4000 |
Tensile Elongation |
D638 |
23°C |
% |
4 |
4 |
3 |
3 |
15 |
|
Flexural Strength |
D790 |
23°C |
MPa |
160 |
230 |
230 |
180 |
170 |
90 |
Flexural Modulus |
D790 |
23°C |
MPa |
4800 |
9000 |
9200 |
7500 |
5300 |
3500 |
Izod Impact Strength |
D256 |
Notched |
MPa |
6 |
10 |
13 |
6 |
5 |
7 |
Rockwell Hardness |
D785 |
R-scale |
KJ/M^2 |
120 |
120 |
120 |
120 |
120 |
115 |
Flammability |
UL94 |
- |
- |
HB |
HB |
HB |
HB |
HB |
HB |
Dielectric Constant |
D150 |
10^6Hz |
- |
3.5 |
3.5 |
3.5 |
3.5 |
3.5 |
3.6 |
Dielectric Dissipation Factor |
D150 |
10^6Hz |
- |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
Volume Resistivity |
D257 |
- |
Ω·CM |
1*10^14 |
1*10^14 |
1*10^14 |
1*10^14 |
1*10^14 |
1*10^14 |
Dielectric Strength |
D149 |
- |
KV/MM |
22 |
22 |
22 |
22 |
22 |
21 |