پلی آمید 6- تقویت شده

KOPLA PA6

SORT

FILLED & REINFORCED GRADE

NEW

KNG1015

KNG1020

KNG1030

KNG1045

KNG1050

KNG1060

KNR1061

KNR1031

OLD

UGN16045

UGN16060

UGN16090

UGN16005

UGN16000

-

USG16045

USG16090

Properties

Test Method

(ASTM)

Condition

unit

GF Reinforced

Specific Gravity

D792

-

-

1.23

1.27

1.36

1.51

1.56

1.68

1.22

1.31

Water Absorption

D570

23°C, Water,

24h

%

1.15

1

0.95

0.8

0.75

0.7

1.3

0.9

Poisson's Ratio

D638

23°C

-

0.35

0.35

0.35

0.35

0.35

0.35

-

-

Molding Shrinkage(1/8')

D955

Flow

%

0.7-1.0

0.6-0.9

0.4-0.7

0.1-0.5

0.1-0.5

0.1-0.3

0.7-1.1

0.4-0.8

Xflow

%

0.9-1.2

0.7-1.1

0.6-0.9

0.4-0.8

0.3-0.7

0.2-0.5

0.9-1.3

0.6-1.0

Melting Point

DSC

-

°C

222

222

222

222

222

222

222

222

Heat Deflection

Temperature

D648

4.6kgf/cm²

°C

220

220

220

220

220

220

210

210

18.6kgf/cm²

°C

205

205

210

215

215

215

190

200

Coefficient of Linear

Thermal Expansion

D696

-

X10^-5 1/K

4.2

3.9

3.2

2

1.8

1.5

-

-

Tensile Strength

D638

23°C

MPa(RH0/RH50)

120/70

145/95

170/110

215/140

225/150

230/160

100

145

Tensile Modulus

D639

23°C

MPa(RH0/RH50)

6100/2900

6600/3800

9600/6200

13100/7300

14600/8600

14600/9000

5100

8300

Tensile Elongation

D638

23°C

%(RH0/RH50)

4/7

3/4

3/4

2/3

2/3

2/3

6

4

Flexural Strength

D790

23°C

MPa(RH0/RH50)

170/

200/150

230/170

350/210

360/270

370/280

145

210

Flexural Modulus

D790

23°C

MPa(RH0/RH50)

4800/2800

5600/3700

7900/5500

13000/7200

14500/8500

14900/9200

4400

7200

Izod Impact Strength

D256

Notched

MPa(RH0/RH50)

-

-

15/24

16/29

17/29

18/29

14

21

Rockwell Hardness

D785

R-scale

KJ/M^2(RH0/RH50)

120/115

120/115

120/115

125/115

125/115

125/115

115

115

Flammability

UL94

-

-

HB

HB

HB

HB

HB

HB

HB

HB

Dielectric Constant

D150

10^6Hz

-

3.8

3.8

3.8

3.8

3.8

3.8

3.8

3.8

Dielectric Dissipation

Factor

D150

10^6Hz

-

0.02

0.02

0.02

0.02

0.02

0.02

0.02

0.02

Volume Resistivity

D257

-

Ω·CM

1*10^15

1*10^15

1*10^15

1*10^15

1*10^15

1*10^15

1*10^15

1*10^15

Dielectric Strength

D149

-

KV/MM

22

22

22

22

22

22

22

22

 

KOPLA PA6

SORT

FILLED & REINFORCED GRADE

NEW

KNT1015

KNT1020

KNT1030

KNT1040

KNT1060

KNT2040

OLD

-

UTN16060

UTN16090

UTN16020

UT160180

-

Properties

Test Method (ASTM)

Condition

unit

MF Filled

Specific Gravity

D792

-

-

1.21

1.25

1.38

1.45

2.05

1.46

Water Absorption

D570

23°C, Water, 24h

%

1.1

1.1

1.1

1.1

1.1

1.1

Poisson's Ratio

D638

23°C

-

0.36

0.36

0.36

0.36

0.36

0.36

Molding Shrinkage(1/8')

D955

Flow

%

0.6-0.8

0.6-0.8

0.5-0.8

0.5-0.8

0.1-0.2

0.5-0.8

Xflow

%

0.7-1.0

0.7-1.0

0.7-1.1

0.7-1.1

0.2-0.5

0.7-1.1

Melting Point

DSC Method

-

°C

222

222

222

222

222

222

Heat Deflection Temperature

D648

4.6kgf/cm²

°C

195

195

200

200

200

200

18.6kgf/cm²

°C

105

105

115

120

120

120

Coefficient of Linear Thermal Expansion

D696

-

X10^-5 1/K

6

6

4

4

-

-

Tensile Strength

D638

23°C

MPa

75

75

75

85

70

50

Tensile Modulus

D639

23°C

MPa

3900

4800

6400

6900

6000

4700

Tensile Elongation

D638

23°C

%

15

4

3

3

2

30

Flexural Strength

D790

23°C

MPa

110

110

120

130

110

90

Flexural Modulus

D790

23°C

MPa

3400

4200

5600

6000

5300

4100

Izod Impact Strength

D256

Notched

MPa

6

6

6

7

3

6

Rockwell Hardness

D785

R-scale

KJ/M^2

120

115

115

115

115

115

Flammability

UL94

-

-

HB

HB

HB

HB

HB

HB

Dielectric Constant

D150

10^6Hz

-

3.6

3.6

3.6

3.6

3.6

3.6

Dielectric Dissipation Factor

D150

10^6Hz

-

0.02

0.02

0.02

0.02

0.02

0.02

Volume Resistivity

D257

-

Ω·CM

1*10^14

1*10^14

1*10^14

1*10^14

1*10^14

1*10^14

Dielectric Strength

D149

-

KV/MM

21

21

21

21

21

21

 

 

KOPLA PA6

SORT

FILLED & REINFORCED GRADE

NEW

KNX1014

KNX1076

KNG1040CW

KNU1061

KNH1012

KNU1061

OLD

-

-

 

UGN16045M25

-

-

Properties

Test Method (ASTM)

Condition

unit

GF & MF

GF &GB

MF & ST

Specific Gravity

D792

-

-

1.27

1.47

1.46

1.48

1

1.25

Water Absorption

D570

23°C, Water, 24h

%

1.2

1

1

1

1

1.1

Poisson's Ratio

D638

23°C

-

0.35

0.35

0.35

0.35

0.35

-

Molding Shrinkage(1/8')

D955

Flow

%

0.6-0.8

0.1-0.5

0.1-0.5

0.1-0.5

0.4-0.6

0.6-0.8

Xflow

%

0.7-1.0

0.4-0.8

0.4-0.8

0.4-0.8

0.6-0.9

0.7-1.0

Melting Point

DSC Method

-

°C

222

222

222

222

222

222

Heat Deflection Temperature

D648

4.6kgf/cm²

°C

210

215

220

215

220

195

18.6kgf/cm²

°C

200

205

210

200

205

105

Coefficient of Linear Thermal Expansion

D696

-

X10^-5 1/K

-

-

-

-

3

-

Tensile Strength

D638

23°C

MPa

100

160

180

130

110

55

Tensile Modulus

D639

23°C

MPa

5500

10300

10500

8600

5900

4000

Tensile Elongation

D638

23°C

%

4

4

3

3

 

15

Flexural Strength

D790

23°C

MPa

160

230

230

180

170

90

Flexural Modulus

D790

23°C

MPa

4800

9000

9200

7500

5300

3500

Izod Impact Strength

D256

Notched

MPa

6

10

13

6

5

7

Rockwell Hardness

D785

R-scale

KJ/M^2

120

120

120

120

120

115

Flammability

UL94

-

-

HB

HB

HB

HB

HB

HB

Dielectric Constant

D150

10^6Hz

-

3.5

3.5

3.5

3.5

3.5

3.6

Dielectric Dissipation Factor

D150

10^6Hz

-

0.02

0.02

0.02

0.02

0.02

0.02

Volume Resistivity

D257

-

Ω·CM

1*10^14

1*10^14

1*10^14

1*10^14

1*10^14

1*10^14

Dielectric Strength

D149

-

KV/MM

22

22

22

22

22

21

همکاران تجاری

  • 1.jpg
  • 2.jpg
  • 6.jpg
  • 7.jpg
  • 8.jpg
  • 9.jpg

محصولات

  • product 2.jpg
  • product 12.jpg
  • product 16.jpg
  • product 14.JPG
  • product 8.jpg
  • product 1.jpg
  • product 4.jpg
  • product 9.jpg
  • product 10.jpg
  • product 15.jpg
  • product 3.jpg
  • product 5.jpg
  • product 6.jpg
  • product 7.jpg
  • product 18.jpg
  • product 11.jpg
  • product 17.jpg